Author: Hans-Jürgen Schwarz
English Translation by Sandra Leithäuser
back to Measures

Abstract[edit]

Increased salt contaminations can be reduced using different methods. These include poultice desalination- also in combination with other methods, the reduction of the salts using a water bath, or methods aided by electric currents. When choosing the method, the protection of the object must always be the first priority. The measures should be accompanied by appropriate investigations to ensure their success.

Introduction[edit]

Desalination denotes the removal of salts and salt-forming ions out of the pore structure of porous materials such as natural stone (sandstones, limestones, tuffs, etc.), brick or terracotta and plaster or wall paintings. Treatments can be carried out in situ on the object, or on movable objects in the workshop.

The most commonly encountered salts are sulphates (Gypsum CaSO42H2O, Mirabilite (Thenardite) Na2SO4•10H2O (Na2SO4), magnesium sulphate (MgSO4•7H2O and other hydrates), chlorides (e.g., NaCl) und nitrates (Niter KNO3 u.a.). In individual cases, different salts can exist beside one another, and a variety of salt-forming ions can be in the pore solution.

Salts can damage the fabric of porous materials and lead to powdering of the surface, sometimes causing substantial loss. The amount of decay and its appearance depend on the kind of crystallizing salts, the amount of salt present, and the environmental conditions. Particularly damaging are climate fluctuations around the Deliquescence point of the salts. In addition, water-soluble salts have an influence on conservation measures such as consolidation, treatment with hydrophobic materials and painting or plastering, often making such action impossible. For these reasons, the reduction of the salt content is an indispensable prerequisite for the success and the durability of a conservation measure apart from reducing the deterioration rate of the object in question.

The desalination/ salt reduction can be executed using several different methods [Sawdy.etal:2006]Title: Desalination—rubbing salt into the wound?
Author: Sawdy, Alison; Heritage, Adrian
Link to Google Scholar
. The use of plaster/ slurries on salt-contaminated objects [Auras:2008]Title: Poultices and mortars for salt contaminated masonry and stone objects
Author: Auras, Michael
Link to Google Scholar
is described elsewhere.

Water bath desalination[edit]

This method is only applicable for objects that can be transported to a workshop, usually sculptures and objects that can be removed from their permanent location.[Franzen.etal:2008]Title: Water bath desalination of sandstone objects
Author: Franzen, Christoph; Hoferick, Frank; Laue, Steffen; Siedel, Heiner
Link to Google Scholar

The salt contaminated object is placed in a bath of cold or slightly warm water. In doing so, the water can circulated and deionized to enhance the desalination process. An easier, but less effective method is to change the water from time to time. The efficiency of the desalination is monitored by measuring the conductivity of the water.

Degree and speed of the desalination depends on the size of the object, the properties of the material (e.g., fine pores or coarsely porous stone), the type and amount of salts and salt-forming ions and their distribution in the pores. Salts concentrated near the surface are removed faster than those from deeper areas. The treatment of life-size figures can take between a few weeks to several months.

On suitable objects, desalination in a water bath has a good chance of success. Specific risk factors are:

  • The saturation of the entire pore structure with water: risk for paint layers;
  • Advanced degree of destruction: flaking of brittle surfaces;
  • Salts with several hydrate phases: phase changes may induce mechanical stresses, which can cause a loss of substance to the object.

A pre-consolidation of brittle surfaces with a suitable strengthening agent, such as silicic acid esters may be possible. Due to this treatment the desalination can in some cases, be considerably delayed.

Poultices for desalination[edit]

Desalination using poultices relies on the principle that salts dissolved in water are transported from the salt-contaminated, porous, mineral building materials into the poultice. The transport of salt solutions can take place both by diffusion and by movement of the fluid. The motion of a fluid is usually triggered by a moisture gradient (capillary action) or by temperature, density and pressure gradients (convection). In contrast, concentration gradients lead to the diffusion of the salt ions. The transport by capillary action (advection) is determined by the pore structure of the building material and is characterized by the water absorption coefficient [Heritage.etal:2008]Title: How do conservators tackle desalination? An international survey of current poulticing methods
Author: Heritage, Adrian; Sawdy, Alison; Funke, Fredericke; Vergès-Belmin, Veronique; Bourges, Anne
Link to Google Scholar
. The transport direction of the ions follows the moisture gradient, i.e., from the humid to the dryer area. The driving force for ion transport by diffusion is the concentration gradient. The ions diffuse in accordance with the concentration gradient, from the higher to the lower concentration. Diffusion also takes place as surface diffusion on the interface. The convective transport is triggered by pressure, density and temperature differences and can be checked via the water permeability or other tests. This transport process occurs preferentially in larger pores (> 0,1 mm), fissures and voids. The processes described above take place in combination. The scale on which the transport processes contribute to the desalination, depends on the properties of the poultice material, on the environmental and procedural conditions. Essentially, the moisture and salt currents are influenced by a complex interplay between moisture condition, salt distribution, the properties and particularly the porosity of the substrate and that of the poultice [Pel.etal:2010]Title: Physical principles and efficiency of salt extraction by poulticing
Author: Pel, Leo; Sawdy, Alison; Voronina, V.
Link to Google Scholar
[Lubelli.etal:2010]Title: Desalination of masonry structures: fine tuning of pore-size distribution of poultices to substrate properties
Author: Lubelli, Barbara; van Hees, Rob P. J.
Link to Google Scholar
. The salt reduction using poultices is the most common method of desalination [Bourges.etal:2008]Title: Comparison and optimization of five desalination systems on inner walls of Saint Philibert church in Dijon, France
Author: Bourgès, Anne; Vergès-Belmin, Veronique
Link to Google Scholar
[Verges-Belmin.etal:2005]Title: Desalination of masonries and monumental sculptures by poulticing: a review
Author: Vergès-Belmin, Veronique; Siedel, Heiner
Link to Google Scholar
. In the last years, important methodical improvements have been achieved, especially due to the EU- project "Desalination" [Sawdy.etal:2008]Title: A review of salt transport in porous media, assessment methods and salt reduction treatments
Author: Sawdy, Alison; Heritage, Adrian; Pel, Leo
Link to Google Scholar
.



Electrochemical desalination[edit]

Electrochemical desalination can be conducted in the workshop or on site, on the object. When introducing electric tension to the object the salt ions migrate to the anode or cathode. The electrodes have to be laid into a poultice or mortared into a gap in the masonry. Basic principles of this method are the processes known as electrokinetics and electroosmosis, respectively. If an electric field is installed with the help of electrodes, the ions migrate to the oppositely charged poles. The electrochemical desalination according to the principle of electroosmosis (including the AET- Aktive Entsalzung und Trocknung- active desalination and drying method) has been a matter of controversial discussion in the literature. For an efficient desalination a number of rod-shaped electrodes are needed, that can be mortared into crevices or drill holes. The distance between electrodes should not be more than 30 cm. A better solution appears to be the use of net shaped electrodes, that are placed in a poultice onto the surface. A major problem consists in producing a similarly good electrical transition on every electrode. Otherwise the current only flows to one electrode, which cannot be verified without special circuits. The applied tension has to be on a scale of several ten volts, this can lead to health and safety issues when used outdoors. The method of desalination only works, if sufficient moisture is present and for this reason the objects have to be kept humid.

Due to the very complicated and not well-established discharge reaction of the ions on the electrodes, a return migration of ion complexes can take place. This particularly applies to ions with amphoteric properties (e. g., magnesium ions). Furthermore, the discharge reaction can cause strong pH fluctuations, leading to a very acidic or a very alcaline environment and to damages in the vicinity of the electrodes.

In the event of a high salt contamination, a new method, developed by Friese can be applied ([Venzmer:1991]Title: Sanierung feuchter und versalzener Wände
Author: Venzmer, Helmuth
Link to Google Scholar
). In such cases the influence of electric fields serves to stop the ion transport in the material. Hence, brick sized suction cups are placed on the surface of the wall. Under vacuum conditions a liquid is led past the sample surface. The liquid moistens the surface and sets the salt ion transport into motion. The salts are virtually washed off the surface and transported away.

Evaluation criteria[edit]

(according to [Snethlage:1994]Title: Entsalzung
Author: Snethlage, Rolf
Link to Google Scholar
)

The presence of soluble salts is nearly always part of the reason why historic building materials are deteriorated. To determine whether a desalination should be carried out, the following points need to be considered:

Evaluation (Risk assessment) of hazards to the substance of objects affected by salt contamination

It is to be balanced, whether the desalination measures may cause greater loss to the substance, than leaving the object in its present condition. If the climate can be stabilized to a degree, so that the salts are not subject to dissolution and recrystallization cycles, it is justifiable not to carry out a desalination.

Usefulness of the desalination

It is necessary to assess whether it is at all possible to carry out a successful desalination. Only if the salts are situated near the surface, can a desalination process be promising. A uniform distrobution of salts at approximately 1% by weight throughout the wall thickness, which commonly occurs in the presence of nitrates, cannot be treated successfully. In such cases other solutions must be considered, e.g., giving the building a different use.

Protection of the original substance

During desalination treatment, risks to the object can arise. For example, incorrectly applied poultices may not be easily removed from the surface and their removal may cause more damage.

Adverse effects on other conservation measures

Low salt concentrations do not compromise the success of other conservation measures. Desalination in such cases may therefore be omitted. However, only a material-specific threshold value for salt contaminations can be specified, because the porosity, pore radius distribution and climate plays an important role. In individual cases decisions have to be made with reference to a survey or condition report. It is known that high concentrations of salts can have adverse effects on consolidation with silicic acid esters or on hydrophobic treatments. Also the durability of the measure will be affected.

Control measures[edit]

To evaluate the effectiveness of the desalination, the salt content in stone, plaster or brick should be measured before and after the treatment.

There are only a few experiences on the desalination of entire buildings. Basically, a satisfactory desalination of any kind can only be expected, if the salts are concentrated near the surface at 1-2 cm depth. With both, poultices and electrochemical methods, the desalination will only reach a few centimeters into the materials.

Example: At "Nürnberger Tor" in Forchheim a NaCl contamination was successful in removing nearly 90% of the salt using a bentonite / sand / cellulose poultice, which was applied twice to the splash zone of the structure. The success of the measure was can be attributed to the fact that the salt was confined to the few outermost centimeters.

Literature[edit]

[Auras:2008]Auras, Michael (2008): Poultices and mortars for salt contaminated masonry and stone objects. In: Ottosen, Lisbeth M.; Rörig-Dalgaard, Inge; Larsen, Poul Klenz; Brajer, Isabelle; Bøllingtoft, Peder; Marciniak, Mette; Svane, Maja (eds.): Salt Weathering on Buildings and Stone Sculptures, Technical University of Denmark, Lyngby, Denmark, 197-217.Link to Google ScholarFulltext link
[Bourges.etal:2008]Bourgès, Anne; Vergès-Belmin, Veronique (2008): Comparison and optimization of five desalination systems on inner walls of Saint Philibert church in Dijon, France. In: Ottosen, Lisbeth M.; Rörig-Dalgaard, Inge; Larsen , Poul Klenz; Brajer, Isabelle; Bøllingtoft, Peder; Marciniak, Mette; Svane, Maja (eds.): Salt Weathering on Buildings and Stone Sculptures, Technical University of Denmark, Lyngby, DenmarkTechnical University of Denmark, Lyngby, Denmark, 29-41.Link to Google ScholarFulltext link
[Franzen.etal:2008]Franzen, Christoph; Hoferick, Frank; Laue, Steffen; Siedel, Heiner (2008): Water bath desalination of sandstone objects. In: Lukasziewicz, J.; Niemcewicz, Piotr (eds.): Proceedings 11th International Congress on Deterioration and Conservation of Stone, Torun, , 881-888.Link to Google ScholarFulltext link
[Heritage.etal:2008]Heritage, Adrian; Sawdy, Alison; Funke, Fredericke; Vergès-Belmin, Veronique; Bourges, Anne (2008): How do conservators tackle desalination? An international survey of current poulticing methods. In: forthcoming (eds.): , .Link to Google Scholar
[Lubelli.etal:2010]Lubelli, Barbara; van Hees, Rob P. J. (2010): Desalination of masonry structures: fine tuning of pore-size distribution of poultices to substrate properties. In: Journal of Cultural Heritage, 11 (1), 10-18, Url, doi:10.1016/j.culher.2009.03.005Link to Google Scholar
[Pel.etal:2010]Pel, Leo; Sawdy, Alison; Voronina, V. (2010): Physical principles and efficiency of salt extraction by poulticing. In: Journal of Cultural Heritage, 11 (1), 59-67, Url, 10.1016/j.culher.2009.03.007Link to Google Scholar
[Sawdy.etal:2006]Sawdy, Alison; Heritage, Adrian (2006): Desalination—rubbing salt into the wound?. In: Oltrogge, D. (eds.): In and Out, Projekt aus Forschung und Lehre Institut für Restaurierungs- und Konservierungswissenschaft Köln, Festschrift zum 20jährigen bestehendes Institutes Köln 2006, SICS Institut für Restaurierungs- und Konservierungswissenschaft Fachhochschule Köln, Cologne, 41-45.Link to Google Scholar
[Sawdy.etal:2008]Sawdy, Alison; Heritage, Adrian; Pel, Leo (2008): A review of salt transport in porous media, assessment methods and salt reduction treatments. In: Ottosen, Lisbeth M.; Rörig-Dalgaard, Inge; Larsen, Poul Klenz; Brajer, Isabelle; Bøllingtoft, Peder; Marciniak, Mette; Svane, Maja (eds.): Salt Weathering on Buildings and Stone Sculptures, Proceedings from the International Conference 22–24 October 2008, National Museum Copenhagen, Denmark,Technical University of Denmark, Lyngby 1-28.Link to Google ScholarFulltext link
[Snethlage:1994]Snethlage, Rolf (1994): Entsalzung, Arbeitsblätter des Bayerischen Landesamtes für Denkmalpflege.Link to Google Scholar
[Venzmer:1991] Venzmer, Helmuth (1991): Sanierung feuchter und versalzener Wände, Verlag für das Bauwesen, BerlinLink to Google Scholar
[Verges-Belmin.etal:2005]Vergès-Belmin, Veronique; Siedel, Heiner (2005): Desalination of masonries and monumental sculptures by poulticing: a review. In: International Journal for Restoration of Buildings and Monuments, 11 (6), 391-407Link to Google Scholar